Our PVC-SiO2 separation has a deeper pore structure. This increases the separator’s porosity, reduces resistance, and improves battery capacity.
PVC battery separators are more porous than 78%. Their maximum pore dimension is 10 microns. They also have an extremely fast wetting speed of the electrolyte of just 2 seconds. It has a resistance of 0.0003O.dm2, one-tenth the standard for ordinary separators. trusted global PVC–SiO2 separator supplier . You can send us an inquiry regarding the HTMLVC-SiO2 separator prices at any moment.
PVC-SiO2 Separator performance:
The Technical Property of the Separator PVC-SiO2:
|Moisture||Porosity||The Electric Resistance||Tensile strength||Max Pore Diameter||The Speed of Wetting||Reduplication of Substance|
|1.5%||84%||0.0005O.dm2||3.47 MPa||8um||3.8||8.9 mL/g|
PVC-SiO2 separator applications:
PVC/SiO2 separators can be used to separate positive and negative electrodes in polymers. They are primarily used in lead-acid battery manufacturing.
PVC-SiO2 Separator in Storage:
PVC-SiO2 separators should be stored in dry, cool environments, away from the elements. This will prevent the formation of oxidative agglomeration due to moisture.
Shipping and Packing of PVC SiO2 Separators:
You can pack it in two plastic bags with the inside.
Packaging of PVC-SiO2 separators: 50 pieces/cart, or as requested
Delivery of powder separator PVC-SiO2: After receipt of payment, items may be sent out either by sea or air.
PVC – SiO2 Separator Property
|Other Titles||PVC separator and battery separator|
|Solubility In Water||N/A|
Information on separators from PVC-SiO2